- Abstract
- Combustion in the 2Co–Ti–Al system was observed by high-speed video recording. It is established that combustion occurs in the frontal mode, and the process parameters are determined. The maximum rate of the combustion temperature increase from the moment of initiation to the maximum value reached 2.7 · 104 K/s. The front propagation velocity calculated from the video recording was 9.4 cm/s. A micro-hotspot mode of combustion of the reaction composition was found. The temperature dependences of the electrical resistivity and magnetic moment of the single-phase Co2TiAl product synthesized in the combustion mode have been measured. For the synthesized Co2TiAl sample, the Curie temperature is Tc = 120 ± 5 K, and the electrical resistivity at room temperature is 1.35 μOhm · m. It is shown that the electrical and magnetic properties of the Co2TiAl alloy obtained in the combustion mode are similar to those of alloys obtained by arc melting.
- Keywords
- самораспространяющийся высокотемпературный синтез высокоскоростная видеосъемка фаза Гейслера Co2TiAl магнитные свойства
- Date of publication
- 15.08.2024
- Year of publication
- 2024
- Number of purchasers
- 0
- Views
- 40
References
- 1. Appel F., Clemens H., Fischer F. // J. Progress Mater. Sci. 2016. V. 81. P. 55. https://doi.org/10.1016/j.pmatsci.2016.01.001
- 2. Долуханян С.К., Алексанян А.Г., Мурадян Г.Н. и др. // Хим. физика. 2021. Т. 40. № 7. С. 76. https://doi.org/10.31857/S0207401X21070037
- 3. De Groot R., Mueller F., Engen P. et al // Phys. Rev. Lett. 1983. V. 50. № 25. P. 2024. https://doi.org/10.1103/PhysRevLett.50.2024
- 4. Васильев А.Н., Бучельников В.Д., Такаги T. и др. // УФН. 2003. Т. 173. № 6. С. 577. https://doi.org/10.3367/UFNr.0173.200306a.0577
- 5. Graf Т., Fecher G., Barth J. et al // J. Phys. D: Appl. Phys. 2009. V. 42. № 084003. https://doi.org/10.1088/0022-3727/42/8/084003
- 6. Перевозчикова Ю.А., Коуров Н.И., Емельянова С.М. и др. // Междунар. журн. прикл. и фундамент. исслед. 2016. № 3−4. С. 539.
- 7. Fadila B., Ameri M., Bensaid D. et al // J. Magn. Magn. Mater. 2018. V. 448. P. 208. https://doi.org/10.1016/j.jmmm.2017.06.048
- 8. Koller M., Chráska T., Cinert J. et al // Mat. Des. 2017. V. 126. P. 351. https://doi.org/10.1016/j.matdes.2017.04.028
- 9. Zhang W., Zhao L., Qian Z. et al // J. Alloys Compd. 2007. V. 431. P. 65. https://doi.org/10.1016/j.jallcom.2006.05.083
- 10. Итин В.И., Найбороденко Ю.С. Высокотемпературный синтез интерметаллических соединений. Томск: Изд-во Том. ун-та, 1989.
- 11. Бусурина М.Л., Сычёв А.Е., Карпов А.В. и др. // Хим. физика. 2020. Т. 39. № 11. С. 39. https://doi.org/10.31857/S0207401X20110023
- 12. Силяков С.Л., Ширяева М.Ю., Беликова А.Ф.и др. // Хим. физика. 2022. Т. 41. № 3. С. 81. https://doi.org/10.31857/S0207401X22030128
- 13. Liang J., Zhu L., Wang L.V. // Light Sci Appl. 2018. V. 7. P. 42. https://doi.org/10.1038/s41377-018-0044-7
- 14. Mukasyan A.S., Hwang S., Sytchev A.E. et al // Combust. Sci. Techn. 1996. V. 115. № 4−6. P. 335. https://doi.org/10.1080/00102209608935535
- 15. Рогачёв А.С., Мукасьян A.C. // Физика горения и взрыва. 2015. Т. 51. № 1. С. 66.
- 16. Кочетов Н.А., Сеплярский Б.С. // Хим. физика. 2023. T. 42. № 3. С. 23. https://doi.org/10.31857/S0207401X23030081
- 17. Rogachev A.S., Vadchenko S.G., Sachkova N.V. et al. // Dokl. Phys. Chem. 2018. V. 478. P. 27. https://doi.org/10.1134/S0012501618020021
- 18. Бусурина М.Л., Сычёв А.Е., Ковалев И.Д. и др. // Физика горения и взрыва. 2020. Т. 56. № 3. С. 78. https://doi.org/10.15372/FGV20200308
- 19. Mizusaki S., Ohnishi T., Ozawa T.C. et al // Trans. Magnеt. 2011. V. 47. № 10. P. 2444. https://doi.org/10.1109/TMAG.2011.2159581
- 20. Щербаков А.С., Прекул А.Ф., Поморцев Р.В. // Письма в ЖЭТФ. 1980. Т. 32. № 6. С. 425.